ACUMER 5000 is a proprietary multifunctional polymer with a molecular weight of 5000 that provides exceptional silica and magnesium silicate scale inhibition.
ACUMER 5000 is Silica and Magnesium Silicate Scale Inhibitor.
ACUMER 5000 is an excellent scale inhibitor and dispersant for silica and magnesium silicate.
ACUMER 5000 has been evaluated under field conditions, allowing up to 300 ppm silica in the recirculating water without scale.
Case histories are available upon request from your local technical representative.
Performance of ACUMER 5000:
Control of silica-based scale is a complex problem due to the many forms of silica species that exist:
Molybdate-reactive silica: frequently referred to as dissolved silica.
Colloidal silica: polymerized silica particles of 0.1 microns or less.
Silica scale: primarily magnesium silicate, but may also be iron or calcium silicate.
Colloidal silica can dissolve to form silicate in the high temperature/high pH environment near a corroding cathodic surface where dissolved oxygen is reduced to hydroxide ions.
These freshly formed silicate anions, added to the dissolved silica already present, can then form magnesium silicate scale (MgSiO3).
In addition, colloidal silica alone can co-precipitate with magnesium hydroxide to form a scale of magnesium silicate having non-stoichiometric ratios of magnesium to silica.
Normally, if silica levels exceed about 180 ppm SiO2 in the recirculation water of a cooling circuit, severe scaling can occur on heat transfer surfaces.
Moreover, the scale that forms is frequently difficult or impossible to remove by conventional means.
ACUMER 5000 has been evaluated under field conditions, allowing up to 300 ppm silica in the recirculating water without scale. Case histories are available upon request from your local technical representative.
Benefits of ACUMER 5000:
Helps keep surfaces clean for maximum heat transfer and enhances the performance of organic corrosion inhibitors.
Has excellent thermal and chemical stability.
Can be formulated at any pH without degradation.
Exhibits a very good stability in the presence of hypochlorite.
Contains no phosphorus, making ACUMER 5000 use acceptable where legislation requires that discharge waters contain low or no phosphorus
Cooling water reuse is frequently limited by a ceiling on the amount of tolerable silica in the recirculation water.
Normally, if silica levels exceed about 180 ppm SiO2, severe scaling can occur on heat transfer surfaces.
Moreover, the scale that forms is frequently difficult or impossible to remove by conventional means.
ACUMER 5000 silica control polymer has now raised that ceiling to at least 300 ppm SiO2,proven by exacting pilot studies and field trials,allowing for greater water reuse than ever before.
ACUMER 5000 polymer prevents silica-based scale formation by dispersing colloidal silica and by preventing magnesium silicate scale formation at the heat transfer surfaces.
Excellent scale inhibition for a variety of applications including cooling circuits, boilers and RO units.
Scale Control / Inhibition: Calcium Carbonate, Calcium Phosphate / Phosphonate, Iron Oxide Dispersion, Silica / Silicate.
Uses of ACUMER 5000:
Industrial water treatment
Applications of ACUMER 5000:
Recirculating cooling circuits:
ACUMER 5000 offers distinct features for the treatment of silica-limited cooling waters,allowing up to at least 300 ppm silica in the recirculating water without scale or corrosion problems.
Boilers:
The excellent hydrothermal stability of ACUMER 5000 makes it an ideal choice for use in controlling magnesium silicate scale in boilers operating up to about 900 psig, although silica may carry over in steam at >600 psig.
Boilers,
Cooling Water,
Membranes.
Chemistry and Mode of Action of ACUMER 5000:
ACUMER 5000 is a proprietary multifunctional polymer with a molecular weight of 5000 that provides outstanding silica and magnesium silicate scale inhibition.
ACUMER 5000 prevents silica-based scale formation by dispersing colloidal silica and by preventing magnesium silicate scale formation at heat transfer surfaces.
ACUMER 5000 is a proprietary multifunctional polymer with a molecular weight of 5000 that provides exceptional silica and magnesium silicate scale inhibition.
ACUMER 5000 helps prevent silica-based scale formation by dispersing colloidal silica and by minimizing magnesium silicate scale formation at heat transfer surfaces.
Performance Control of silica-based scale is a complex problem due to the many forms of silica species.
Molybdate-reactive silica: frequently referred to as dissolved silica.
Colloidal silica: polymerized silica particles of 0.1 microns or less.
Silica scale: primarily magnesium silicate, but may also be iron or calcium silicate.
Colloidal silica can dissolve to form silicate in the high temperature/high pH environment near a corroding cathodic surface where dissolved oxygen is reduced to hydroxide ions.
These freshly formed silicate anions, added to the dissolved silica already present, can then form magnesium silicate scale (MgSiO3).
In addition, colloidal silica alone can co-precipitate with magnesium hydroxide to form a scale of magnesium silicate having non stoichiometric ratios of magnesium to silica.
Normally, if silica levels exceed about 180 ppm SiO2 in the recirculation water of a cooling circuit, severe scaling can occur on heat transfer surfaces.
Moreover, the scale that forms is frequently difficult or impossible to remove by conventional means.
Formation of Silica-Based Scale of ACUMER 5000:
Silica forms particles with different structures depending upon the pH, presence of other ions and process by which the particles are formed.
The three main forms of silica encountered in cooling water are:
Molybdate-reactive silica: frequently referred to as dissolved silica.
Colloidal silica: polymerized silica particles of 0.1 micron or less.
Silicate scale: primarily magnesium silicate, but may also be iron or calcium silicate.
Colloidal silica, which forms when the solubility level of silica is exceeded, is difficult to measure under field conditions, and a total silica mass balance cannot be achieved with a simple field test.
The most effective method of determining total silica is described in “Standard Methods for the Examination of Water and Wastewater”, 17th edition (Method 4500-SiC).
Total Silica Test for High-Silica Waters”
As the colloidal silica passes into the Nernst diffusion layer at the heat transfer surface, ACUMER 5000 dissolves and acquires a negative (anionic) charge.
Polyvalent cations, especially magnesium, tend to react with these anionic colloidal particles effectively “gluing” them together and ultimately forming a hard, glassy magnesium silicate scale.
Shows how colloidal silica can dissolve to form silicate in the high temperature/high pH environment near a corroding cathodic surface where dissolved oxygen is reduced to hydroxide ions.
These freshly formed silicate anions, added to the dissolved silica already present, can then form magnesium silicate scale (MgSiO3).
In addition, colloidal silica alone can coprecipitate with magnesium hydroxide to form a scale of magnesium silicate having non-stoichiometric ratios of magnesium to silicate.
Mechanism for Controlling Silica of ACUMER 5000:
The remarkable properties of ACUMER 5000 polymer derive in large part from ACUMER 5000 three distinctive functionalities.
The weak acid (carboxylate) group provides a means of attaching the polymer to metal ions in solution and to the surfaces of particles or crystals.
This enables the polymer to act as a dispersant to prevent agglomeration and deposit formation as well as stabilizing contaminants.
The strong acid (sulfonate) contributes to this process by increasing the solubility and charge density of the polymer which enhances electrostatic repulsion of particles.
What sets ACUMER 5000 polymer apart, however, is a unique third set of functionalities, based on balanced hydrophilicity and lipophilicity (hydrophobicity).
Where the other functionalities operate primarily through charge-transfer, this so-called HLB functionality promotes physical adsorption on the surfaces of contaminant particles especially at higher temperatures.
By promoting adsorption, this third type of functionality also contributes to the strength of the energy barrier (or the net repulsive force) created by the polymer around the silica particle.
ACUMER 5000 polymer adsorbed on the colloid surfaces provides an energy barrier that prevents precipitation and agglomeration.
Moreover, even if the silica particles precipitate, they are spaced too far apart for magnesium or redissolved silicate anions to bind them together.
As a result, the scale formed by these particles will be powdery and, thus, easier to remove.
Typical Properties of ACUMER 5000:
Appearance: Dark yellow to brown clear solution*
Average molecular weight: 5000 (Mw)
Total solids (%): 45
Active solids (%): 42
pH as is (at 25°C): 2.5
Bulk density (at 25°C): 1.20
Viscosity Brookfield (mPa.s/cps at 25°C): 400
Neutralization: 0.13 g of NaOH (100%) per g of ACUMER™ 5000
pH 2.1 to 2.6
Brookfield Viscosity, cp 700 max.
Specific Gravity 1.2
Bulk Density, lb/gal (g/cc) 10 (1.19)
Lb (Kg) of 100% NaOH to
neutralize 1 lb (kg) of polymer 0.131
*A slight haze may appear; this does not affect the intrinsic properties of ACUMER 5000 or its performance.